Selem Stainless steel is one of the notable provider and vendor for excellent Stainless Steel 310S Sheets Plates Coils, which are delivered in little amounts, contain costly combinations, and are regularly sold distinctly by the kilogram and by their individual exchange names. By and large Stainless Steel 310 Sheets are hard, wear – safe, intense, and inactive to neighborhood overheating, and regularly built to specific assistance prerequisites. Treated Steel 310 Plates additionally must be dimensionally steady during solidifying and hardening. Hardened Steel 310 Coils contain solid carbide formers, for example, tungsten, molybdenum, vanadium, and chromium in various blends and frequently cobalt or nickel to improve high – temperature execution. On a fundamental level, Stainless Steel 310S Sheets are framed into either level items or long items, the two of which have either hot – moved, cold – shaped or covered surface. Treated Steel 310S Plates are moved from sections, which are viewed as a semi – completed item and are regularly not sold. Greatest components of these Stainless Steel 310S Coils fluctuate with accessible piece sizes or ingot loads and with the spans of introduced moving factories and assistant.
Specification | ASTM A240 / ASME SA240 |
Dimension Standard | JIS, AISI, ASTM, GB, DIN, EN, etc. |
Width | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc |
Length | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc. |
Thickness | 0.3 mm to 120 mm |
Form: | Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc. |
Surface Finishing : | Hot rolled plate (HR), Cold rolled sheet (CR),2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, Chequered, embossed, hair line, sand blast, Brush, etching, SATIN (Met with Plastic Coated) etc. |
STANDARD | UNS | JIS | WERKSTOFF NR. |
SS 310S | S31008 | SUS 310S | 1.4845 |
Grade |
UNS No |
Old British |
Euronorm |
Swedish SS |
Japanese JIS |
||
BS |
En |
No |
Name |
||||
310S |
S31008 |
310S16 |
- |
1.4845 |
X8CrNi25-21 |
2361 |
SUS 310S |
Grade |
C |
Mn |
Si |
P |
S |
Cr |
Mo |
Ni |
N |
|
310S |
min. max. |
- 0.08 |
- 2.00 |
- 1.50 |
- 0.045 |
- 0.030 |
24.0 26.0 |
- |
19.0 22.0 |
The mechanical properties of grade 310S Stainless Steel Sheet are displayed in the following table.
Grade |
Tensile Strength (MPa) min |
Yield Strength 0.2% Proof (MPa) min |
Elongation (% in 50mm) min |
Hardness |
|
Rockwell B (HR B) max |
Brinell (HB) |
||||
310S |
515 |
205 |
40 |
95 |
217 |
Grade |
Density (kg/m3) |
Elastic Modulus (GPa) |
Mean Coefficient of Thermal Expansion(μm/m/°C) |
Thermal Conductivity(W/m.K) |
Specific Heat 0-100°C (J/kg.K) |
Electrical Resistivity (nΩ.m) |
|||
0-100°C |
0-315°C |
0-538°C |
at 100°C |
at 500°C |
|||||
310S |
7750 |
200 |
15.9 |
16.2 |
17.0 |
14.2 |
18.7 |
500 |
720 |