salem stainless steel is engaged with Manufacturing Exporting of top notch tempered steel 316L plates, treated steel 316L plates, hardened steel 316 loops in thickness of 0.3mm to 120mm. that have discovered broad applications in different enterprises. We likewise bargain in Nickel and copper combination, Stainless Duplex Steel, Carbon Alloy Steel, are the materials which are utilized for planning of hardened steel sheet, plate and loop. Compound 316L opposes air consumption, just as, reasonably oxidizing and decreasing situations. It likewise opposes consumption in contaminated marine climates. The combination has astounding protection from intergranular consumption in the as-welded condition. Amalgam 316L has superb quality and sturdiness at cryogenic temperatures.
| specification | ASTM A240 / ASME SA240 |
| Standard | ASTM, AISI, SUS, JIS, EN, DIN, GB, ASME, etc |
| Technique | Cold/Hot Rolled 316 Stainless Steel plate |
| Grade | ASTM A240 Grade 316 |
| Type | ASTM A240 Type 316 Plate |
| Size | 6000mm x 2000mm / 4000mm x 2000mm / 4000mm x 1500mm / 3000mm x 1500mm / 2500mm |
| Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc. |
| Form | SS 316 Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) |
| STANDARD | UNS | JIS | WERKSTOFF NR. | AFNOR | BS | GOST | EN |
| SS 316L | S31603 | SUS 316L | 1.4404 | Z7CND17‐11‐02 | 316S11/316S13 | - | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 316L | min. | – | – | – | – | – | 16.0 | 2.00 | 10.0 | – |
| max. | 0.08 | 2.00 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 | |
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 316L | 515 | 205 | 40% | 95 | 217 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (m/m/0C) | Thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
| 0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
| 316L | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |