316L tempered steel plates are a piece of the austenitic group of treated steel and is the most broadly utilized assortments of impeccable plate. 316L evaluations contain a more significant level of Nickel than 304 giving it an improved consumption opposition more than 304 evaluations. 316L plate is a decent choice for marine applications because of a decent environmental erosion opposition. 316L is a low carbon alteration to 316 evaluation. 316L are austenitic hardened steels that contain molybdenum, which expands their protection from numerous concoction corrodents and marine conditions. 316L is an additional low carbon adaptation of 316 treated steel. These materials are progressively impervious to general consumption and setting/cleft than traditional austenitic treated steels. They additionally offer higher downer, worry to-burst and elasticity at raised temperatures, brilliant consumption opposition and quality properties, and they are appropriate for created or framed applications.
Grade | 316L |
Sheet Finishing | 2B, 2D, HR, CR, BA (No. 8), Satin (Met with PVC Coated) |
Plate in Form of | Coils, Foils, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) Etc. |
Value Added Service | Cladding, Heat Treatment, Annealed |
Thickness | 0.3 mm To 120 mm |
Specification: | A-240 |
Manufacturer: | Jindal, Acroni, Columbus, Acerinox, Thysenkrupp, Posco, Aperam, BRG etc. |
STANDARD | UNS | JIS | WERKSTOFF NR. | AFNOR | BS | GOST | EN |
SS 316L | S31603 | SUS 316L | 1.4404 / 1.4435 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
316L | min. | – | – | – | – | – | 16.0 | 2.00 | 10.0 | – |
max. | 0.08 | 2.00 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 |
The mechanical properties of grade 316L Stainless Steel Sheet are displayed in the following table.
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
316L | 515 | 205 | 40% | 95 | 217 |
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (m/m/0C) | Thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
0-100°C | 0-315°C | 0-538°C | at 100°C | at 500°C | |||||
316L | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |