Salem Stainless Steel is a notable firm that fares and appropriates a wide scope of SS 321 Sheets Plates Coils, which reacts well to solidifying by cool working. The measure of titanium content required in Stainless Steel 321 Sheets is demonstrative of the item level of carbon. Hardened Steel 321 Plates is commonly utilized for parts which are irregularly warmed up to 1500 deg F alongside for nonstop assistance the amalgam regards 1650 deg F. The high erosion obstruction of Stainless Steel 321 Coils depends on the arrangement of a homogeneous, smaller aloof layer superficially. Hardened Steel 321 Sheets has great welding attributes; and post-weld tempering isn't typically required to reestablish its magnificent exhibition in a wide scope of destructive conditions.
| Item | 321 Stainless Steel Sheet(Hot rolled, cold rolled) |
| Standard | ASTM A240, JIS4304-2005, ASTM A167, EN10088-2-2005, GB/T3280-2007, etc |
| Surface | the surface and finish of 321 Stainless Steel Sheet: 2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand blast, Brush, etching, etc |
| Thickness | 0.01~200mm |
| Width | 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc |
| Length | 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc |
| Brand: : | Indian Origin, European Origin, Japanese Origin, US Origin, Korea Origin, Thailand Origin, Taiwan Origin |
| STANDARD | WERKSTOFF NR. | UNS | JIS | AFNOR | BS | GOST | EN |
| SS 321 | 1.4541 | S32100 | – | – | – | – | – |
|
Grade |
UNS No |
Old British |
Euronorm |
Swedish SS |
Japanese JIS |
||
|
BS |
En |
No |
Name |
||||
321 |
S32100 |
321S31 |
58B, 58C |
1.4541 |
X6CrNiTi18-10 |
2337 |
SUS 321 |
|
Grade |
C |
Mn |
Si |
P |
S |
Cr |
Mo |
Ni |
N |
Other |
|
|
321 |
min. max |
- 0.08 |
2.00 |
0.75 |
0.045 |
0.030 |
17.0 19.0 |
- |
9.0 12.0 |
0.10 |
Ti=5(C+N) 0.70 |
|
Grade |
Tensile Strength (MPa) min |
Yield Strength 0.2% Proof (MPa) min |
Elongation (% in 50mm) min |
Hardness |
|
|
Rockwell B (HR B) max |
Brinell (HB) max |
||||
321 |
515 |
205 |
40 |
95 |
217 |
|
Grade |
Density (kg/m3) |
Elastic Modulus (GPa) |
Mean Coefficient of Thermal Expansion (μm/m/°C) |
Thermal Conductivity (W/m.K) |
Specific Heat 0-100°C (J/kg.K) |
Electrical Resistivity (nΩ.m) |
|||
|
0-100°C |
0-315°C |
0-538°C |
at 100°C |
at 500°C |
|||||
321 |
8027 |
193 |
16.6 |
17.2 |
18.6 |
16.1 |
22.2 |
500 |
720 |