Find below the search results for the material you've specified. Please note here this information is NOT to be used for design purposes, and in no event shall MSO be liable for any damages arising from the misuse of this information
Below is a comprehensive list of our alloys arranged by type. More detailed information can be found on each alloys specific page. All of our products are purchased to normal industry standards and come with material test reports (MTR) also known as material certifications.
C-276 is a wrought corrosion-resistant alloy. A prime advantage of this alloy is that it generally does not require solution heat treatment after welding. It resists the formation of grain boundary precipitates that would degrade corrosion resistance.
Chemical process equipment and desulfurization of flue gas equipment.
Good machinability, although the alloy work hardens as is true of the nickel base alloys in general.
Can be cold worked by all conventional methods.
Very good corrosion resistance to oxidizing and reducing acids. The alloy also has excellent resistance to stress-corrosion cracking and to pitting, as well as being very resistant to chlorine gas or compounds corrosion. Boiling HCl acid (2% concentra)
Weldable by all common methods except that excessive heat input should be avoided. Can be used in the "as-welded" condition without further heat treatment for most corrosive applications.
Solution heat treatment is done at 2050 F followed by a rapid quench. The alloy is supplied in this condition. If hot forming or forging is done then the parts should be solution heat treated, if possible, before use.
The alloy can be forged or hot-upset by conventional means.
Can be hot formed or extruded. Should be solution heat treated following hot forming.
Readily cold worked by conventional methods.
Normally supplied and use in the solution treated condition, a 2050 F soak followed by rapid quench.
Not normally done. The alloy is used in solution treated condition.
Not applicable to this alloy.
Hardened by cold working only.
"U" notch impact strength at -320 F of 263 ft. lbs. in solution treated condition.